Crystal Structure and Spectroscopic Properties of a New Ternary Tungstate Li3Ba2Ho3（WO4）8
Author(s): ZENG Xiao-Ling a, b ZHANG Ji-Ye a CHEN Da-Gui a HUANG Feng a②② a b
Pages: 33-38
Year: 2013 Issue: 1
Journal: Chinese Journal of Structural Chemistry
Keyword: Li3Ba2Ho3(WO4)8; crystal structure; crystal growth; optical properties;
Abstract: A single crystal of Li3Ba2Ho3(WO4)8 was obtained from a flux of Li2WO4 under an air atmosphere. The structure of the pure crystal was determined by single-crystal X-ray diffraction method. It crystallizes in the monoclinic system, space group C2/c with a = 5.240(4), b = 12.790(10), c = 19.247(15), β = 91.921(15)°, V = 1289.1(18)3, Z = 2, Mr = 2773.09, Dc = 7.144 g/cm3, μ = 47.732 mm-1, Rint = 0.0693, F(000) = 2340, the final R = 0.0472 and wR = 0.1221 for 1535 observed reflections (I > 2σ(I)). The Li3Ba2Ho3(WO4)8 has a high structure disorder with one 8f site shared by Li(1) and Ho ions with occupancy of 0.25 and 0.75, respectively. The fundamental structure is constituted by distorted square antiprisms Ho/Li(1)O8 with C1 symmetry, distorted Li(2)O6 octahedra and BaO10 polyhedra. The optical properties were investigated by IR and absorption spectroscopy, and the emission cross sections and gain cross sections of 5I7 → 5I8 of Ho3+ were calculated.
Pages: 33-38
Year: 2013 Issue: 1
Journal: Chinese Journal of Structural Chemistry
Keyword: Li3Ba2Ho3(WO4)8; crystal structure; crystal growth; optical properties;
Abstract: A single crystal of Li3Ba2Ho3(WO4)8 was obtained from a flux of Li2WO4 under an air atmosphere. The structure of the pure crystal was determined by single-crystal X-ray diffraction method. It crystallizes in the monoclinic system, space group C2/c with a = 5.240(4), b = 12.790(10), c = 19.247(15), β = 91.921(15)°, V = 1289.1(18)3, Z = 2, Mr = 2773.09, Dc = 7.144 g/cm3, μ = 47.732 mm-1, Rint = 0.0693, F(000) = 2340, the final R = 0.0472 and wR = 0.1221 for 1535 observed reflections (I > 2σ(I)). The Li3Ba2Ho3(WO4)8 has a high structure disorder with one 8f site shared by Li(1) and Ho ions with occupancy of 0.25 and 0.75, respectively. The fundamental structure is constituted by distorted square antiprisms Ho/Li(1)O8 with C1 symmetry, distorted Li(2)O6 octahedra and BaO10 polyhedra. The optical properties were investigated by IR and absorption spectroscopy, and the emission cross sections and gain cross sections of 5I7 → 5I8 of Ho3+ were calculated.
Related Articles