Reason analysis on the foaming phenomenon of high temperature oxidation on the surface of high strength ship plate
Author(s): 
Pages: 28-31
Year: Issue:  2
Journal: Research on Iron and Steel

Keyword:  high strength ship plateblisteringdiffusionoxide scale;
Abstract: In order to solve problems of high-temperature oxidation blistering in highstrength ship plate surface for a company product,laboratory methods of using hightemperature oxidation was adopted to study the phenomenon of high-temperature oxidation blistering in high-strength ship plate surface.The results indicated that oxidation blistering phenomenon of high strength ship plate was related to its high carbon content.By observing the blistering phenomenon of the sample surface,the blistering of the samples surface was occurred when the temperature was higher than950 ℃,and it was also found that the iron oxide bubble phenomenon was lower on the smooth surface of the samples.