Effect of microstructure on slag resistance of Al2 O3-Cr2 O3 bricks
Pages: 188-193
Year: Issue:  3
Journal: Refractories

Keyword:  alumina-chrome bricksslag resistancemicrostructurestatic crucible methodrotary slag method;
Abstract: The slag resistance of two Al2 O3-Cr2 O3 bricks (with 10 mass%Cr2 O3 )A and B were researched using static crucible method and rotary slag method,respectively.The results show that,two Al2 O3-Cr2 O3 bricks have similar properties such as apparent porosity,bulk density,thermal shock resistance,and chem-ical compositions.Brick B has higher strength than brick A.Compared with brick B:brick A has smaller in-ner pores,because the white corundum aggregates in brick A are smoother and denser with continuous particle size distribution;Al2 O3-Cr2 O3 solid solution in brick A is smaller,crossing and forming net structure with small gaps,which reduces the penetration and wear of slag to refractories,meaning that brick A has better slag resistance than brick B.It’s obvious that optimizing microstructure is an effective way to im-prove the slag resistance of Al2 O3-Cr2 O3 materials.
Related Articles
No related articles found