STUDY OF IMPROVING CORROSION RESISTANCE OF TIB2-BASED INERT CATHODE
Author(s): 
Pages: 35-37
Year: Issue:  12
Journal: LIGHT METALS

Keyword:  二硼化铁二硅化钼惰性阴极寿命;
Abstract: 用冷压烧结法制造了TiB2-MoSi2惰性阴极,得到致密的二硼化钛基惰性阴极试样.在电解实验后,通过对二硼化铁阴极的表面和剖面的电子显微分析,发现铝液对此种惰性阴极的湿润性好于电解质对惰性阴极的湿润性,避免了电解质与阴极表面的接触,发现惰性阴极的腐蚀为电解质对阴极晶界的腐蚀,测得腐蚀速度为2.22mm/a,证明其耐蚀性能良好.