Effect of composite antioxidant additions on properties of Al2O3-SiC-C castables
Author(s): 
Pages: 345-347
Year: Issue:  5
Journal: Refractories

Keyword:  composite antioxidantiron trough castablesalumina-silicon carbide-carbon castablesthermal shock resistance;
Abstract: 以电熔棕刚玉为骨料,电熔棕刚玉粉、活性α-Al2O3微粉、黑碳化硅粉、球状沥青、SiO2微粉、纯铝酸钙水泥等为基质料,配以质量分数为2%、2.3%、2.6%、2.9%的复合抗氧化剂,搅拌均匀制备成Al2O3-SiC-C质浇注料.外加5%(w)的水搅拌3~5 min后,检测浇注料的流动性;经振动成型、养护、脱模、干燥后,于1 500℃空气气氛中热处理3h,测定热处理后试样的质量损失率、体积密度、显气孔率、常温耐压强度、常温抗折强度和抗热震性.结果表明:随着复合抗氧化剂加入量(w)从2%增加到2.9%,浇注料的流动性变化不大并且保持较高的水平,显气孔率、体积密度和常温强度变化不大,质量损失率从1.14%减小到0.35%,氧化层厚度逐渐减小;复合抗氧化剂加入量为2.9%(w)的试样热震后耐压强度仍保持在70 MPa左右,具有较好的抗热震性.