Thermal load reaction of continuous casting tundish coating
Author(s): 
Pages: 334-337
Year: Issue:  5
Journal: Refractories

Keyword:  中间包涂料显微结构烧结;
Abstract: 采用X射线衍射仪、扫描电子显微镜和微区能谱分析等,研究了一种中间包涂料在使用后的显微形貌和物相组成变化,探讨了其变化的原因.认为中间包涂料在使用后生成了大量钙镁橄榄石等低熔点物质是导致涂料烧结严重的主要因素,并提出了生产中间包涂料时少加SiO2微粉以控制涂料热负荷反应的改进建议.