Homogenization and Recrystallization of Al-6Mg Alloys with and without Sc and Zr
Author(s): 
Pages: 600-603
Year: Issue:  5
Journal: JOURNAL OF RARE EARTHS

Keyword:  aluminum magnesium alloysscandiumzirconiumhomogenizationrecrystallizationrare earths;
Abstract: Plates of Al-6Mg alloys with and without scandium were prepared by semi-continuous cast, homogenization, hot-rolled, cold-rolled and annealing. Based on studying of effects of temperature and time on hardness and conductivity during homogenization, it was found that homogenization of ingot with Sc and Zr can result in dispersion strengthening. Recrystallization temperature of alloys was studied by hardness method and optical metallographic method. Staring recrystallization temperature of Al-6Mg alloys with Sc and Zr is 375 ℃, increasing by 150 ℃ than Al-6Mg alloys without Sc and Zr. Mechanical properties (σb, σ0.2, δ) of hot-rolled alloy with Sc and Zr are 400 MPa, 280 MPa and 18%; cold-rolled and anneal alloy with Sc and Zr are 420 MPa, 310 MPa and 12% respectively.